Help with polish sequence

9

99MONGUSE

New member
Currently I use 105(if needed) and then 205 with a foam pad on my Makita rotary. I am in the market for a DA polisher (I would like a FLEX but I think a PC 7424xp will be fine) and I think I would benefit from a finer polish after the 205 before I apply a sealant. I was thinking about getting some Klasse AIO and Klasse sealant and then using a good carnuba.



How are you all applying the Klasse AIO...are you using a DA or what. I am looking for a finishing polish after the MEG 205 that is be used with a DA. What would you recommend to use after the 205 for finish polish prior to sealing and waxing? I would even consider two more step of polish after the 205 if that will make the outcome that much better.
 
I would follow with Men. PO85RD instead of the Klasse. Then apply your sealant (I like BFWD) or a good carnuba like Sourveran.
 
99MONGUSE- I too would use some finishing polish from Menzena. IF you really think it'll be of benefit.



Regarding the KSG, I'd much rather get a few more layers of KSG on there than top it with a wax.



Note that the KAIO is basically a "synthetic cleaner wax". Zero functional cut on most any paint and it doesn't leave much of anything behind either. I consider it just a paint cleaner and base for other products like KSG.



Wonder if you'd like Zaino's AIO or Autoglym SRP better :think: Anyhow...



I do KAIO via machine with a zero-cut polishing pad (just a personal preference, but I like that more porous pad a lot better than a tighter finishing pad for this) and speed 4-4.5 on the PC.



I do KSG by hand as I just can't get a thin enough application via machine and I end up wasting product too, so there's no benefit and considerable downside IME. If you want to try it, I'd sure recommend the gold LC pad.
 
You must log in or register to reply here.